K 2010 Trade press conference June 22 and 23, 2010 in Frankenthal, Germany

81

Two-component system for more individualized films
A two-component concept that differs from Styrolux HS 70 is being implemented for the first time: with Styrolux T (T = toughness) and Styrolux S (S = stiffness), this concept offers two new Styrolux grades with which the desired property profile of the shrink film can be set when the processor blends them, and only once they are put together do they yield the film material “Styrolux T/S”.

Natural shrinkage even lower: Higher storage stability
In the blended T/S products, the T component provides basic properties such as toughness and good stretchability, while the S component improves the stiffness of the film as well as its storage stability. The latter is determined by the so-called natural shrinkage that the material undergoes after the stretching procedure. This value is ascertained in a 21-day storage test at 40 degrees Celsius [104 degrees Fahrenheit]. A one-to-one mixture of Styrolux T and Styrolux S, for instance, yields a film that is 25 to 30 percent stiffer and that exhibits a natural shrinkage that is about 50 percent less than a corresponding film made of Styrolux HS 70.

Greater stiffness – high final shrinkage – lower gel content
Films made on the basis of Styrolux T/S exhibit an unparalleled level of transparency and brilliance. Like Styrolux HS 70, Styrolux T/S films are particularly well-suited for the technology of transverse stretching (TD = transverse direction). TD films allow shapes having widely varying radii or unusual designs to be shrink-labelled by sleeve technology.

The new product formulation has succeeded in retaining the familiar, well balanced shrinkage curve of Styrolux HS 70, along with a very high final shrinkage of more than 70 percent at 90 degrees Celsius [194 degrees Fahrenheit]. The uniform, moderate rise of the shrinkage curve permits well-controlled shrink-labelling over a very broad processing range, whereas the high final shrinkage makes it possible to decorate even the most complex of shapes.

Like Styrolux HS 70, the T/S film products stand out for very high efficiency and processing reliability. Owing to the relatively low density, approximately 30 percent more film per kilogram of plastic can be produced than, for example, with PET-G. Moreover, when provided with higher percentages of the S component, the Styrolux T/S films can reach the level of stiffness of PET shrink films.

The two-component concept and the systematic adjustability of the film properties in terms of toughness and stiffness have enabled BASF to respond to customer demands, to their system concepts and to the brand owners, all of which vary considerably from one region to another.

The gel count of Styrolux HS 70, which is already very low, has been reduced even further in the films based on the innovative Styrolux T and S components, thanks to their high thermal stability. T/S films thus meet the requirements of even the most demanding markets.

New perspectives for MD technology
The new Styrolux T/S films not only are suitable for transverse stretching processes but, as so-called MD films, they also yield high-quality products. Stretching films in the extrusion direction (machine direction = MD) as is done in band labelling technology is simpler from the standpoint of the machinery employed and thus correspondingly cheaper. With the roll-on-shrink-on method – ROSO for short – the film label is wrapped around the bottle in the form of a band, fixed by glue and then shrunk onto the bottle under the effect of heat.

When it comes to the products, the ROSO method used to be limited almost exclusively to polypropylene (PP) and to just a few suppliers. The low shrinkage of classic PP-MD shrink films – 20 percent at the maximum at temperatures up to 100 degrees Celsius [212 degrees Fahrenheit] – restricted the use of this method to bottles with simple shapes. Due to its low shrinkage, a PP-MD film cannot tightly enough hug the contour of complex shapes that have greatly varying radii. Creases are formed and the band label does not adhere properly.

The new T/S shrink-film products, but also the proven Styrolux HS 70 and the highly transparent Styrolux grade 3G 46 first introduced onto the market in 2006, open up completely new perspectives for the MD method. These films can achieve shrinkage levels of as much as 45 percent at temperatures of up to 100 degrees Celsius [212 degrees Fahrenheit], and even up to 65 percent at temperatures between 100 and 120 degrees Celsius [212 to 248 degrees Fahrenheit]. In this context, shrink films based on Styrolux 3G 46, which only reach their maximum shrinkage at a temperature above 100 degrees Celsius [212 degrees Fahrenheit], are especially easy to process in hot-air shrink tunnels. MD films on the basis of Styrolux HS 70 or of the new T/S components already attain their highest shrinkage at lower temperatures. This is why they lend themselves for shrink-labelling in steam tunnels.

The significantly higher final shrinkage of the MD Styrolux films means that it is also possible to tightly shrink-label complex shapes such as contoured bottles that have large radius differences, a realm that up until now had been the exclusive domain of TD sleeve films.

In cooperation with leading machine and film manufacturers, it could be demonstrated that Styrolux MD films run very smoothly on existing labelling stations that currently work almost exclusively with ROSO-PP films. Moreover, newer methods such as the hot-sealing of the seams on laser equipment made by the Italian company Sacmi or the hot bar sealing method of Alfa Sidel all yield very good results with Styrolux MD films.

The impact, resilience, and growth of responsible packaging in a wide region are daily chronicled by Packaging South Asia.

A multi-channel B2B publication and digital platform such as Packaging South Asia.is always aware of the prospect of new beginnings and renewal. Its 16-year-old print monthly, based in New Delhi, India has demonstrated its commitment to progress and growth. The Indian and Asian packaging industries have shown resilience in the face of ongoing challenges over the past three years.

As we present our publishing plan for 2023, India’s real GDP growth for the financial year ending 31 March 2023 will reach 6.3%. Packaging industry growth has exceeded GDP growth even when allowing for inflation in the past three years.

The capacity for flexible film manufacturing in India increased by 33% over the past three years. With orders in place, we expect another 33% capacity addition from 2023 to 2025. Capacities in monocartons, corrugation, aseptic liquid packaging, and labels have grown similarly. The numbers are positive for most of the economies in the region – our platform increasingly reaches and influences these.

Even given the disruptions of supply chains, raw material prices, and the challenge of responsible and sustainable packaging, packaging in all its creative forms and purposes has significant headroom to grow in India and Asia. Our context and coverage engulf the entire packaging supply chain – from concept to shelf and further – to waste collection and recycling. We target brand owners, product managers, raw material suppliers, packaging designers and converters, and recyclers.

In an admittedly fragmented and textured terrain, this is the right time to plan your participation and marketing support communication – in our impactful and highly targeted business platform. Tell us what you need. Speak and write to our editorial and advertising teams! For advertisement ads1@ippgroup.in , for editorial info@ippgroup.in and for subscriptions subscription@ippgroup.in

– Naresh Khanna

Subscribe Now